In order to
improve the heat resistance, the aromatic amine is added in the
polyamide - epoxy resin formulation and modified products thereof,
and heat curing of. Polyamide curing conducted at ambient
temperature slowly, if adding 1-3 parts per hundred parts of phenol
or DMP-30 curing accelerating.
200 brown-red liquid amine value of 215 + /-15KOHmg equivalent / g
at viscosity 20-80pa.s/40 ° C per 100 parts by standard resin cured
with 40-100 parts: room temperature for 24 hours or 60 ℃ 3 hours.
250 type C36 brown-red liquid amine value of 240-260KOHmg equivalent
/ g viscosity 8000-25000cp/40 ℃ density per 100 parts 0.94-0.98g/cm3
25 ℃ standard resin cured with 40-100 copies: 24 hours at room
temperature or 60 ℃ 3 hours .
300 brown-red liquid amine value of 305 + /-15KOHmg equivalent / g
viscosity 6-20pa.s/40 ℃ (8000-12000 cp/40 ℃) density per 100
standard 0.94-0.98g/cm3 25 ℃ resin with 40 - 100 parts of curing: 24
hours at room temperature or 60 ℃ 3 hours.
400 type red brown liquid amine value of 200 + /-20KOHmg equivalent
/ g at viscosity 15-50pa.s/40 ° C per 100 parts by standard resin
cured with 40-100 parts: room temperature for 24 hours or 60 ℃ 3
hours.
V115 the standard resin per 100 parts of the amine value of 238 with
40-60 parts of cure: 24 hours at room temperature or 60 ℃ 3 hours.
Heat distortion temperature 45 ℃ with flexural strength 750Kg/cm2
compressive strength 410Kg/cm2 of elongation of 8% Brinell hardness
50-60
203 brown liquid amine value of 200 + /-20KOHmg equivalent / g at
viscosity 1-5pa.s/40 ° C per 100 parts by standard resin cured with
40-100 parts: room temperature for 24 hours or 60 ℃ 3 hours.
V125 amine value of 345 per 100 parts of a standard resin with 40-60
parts of cure: 24 hours at room temperature or 60 ℃ 3 hours. Heat
distortion temperature of 70-85 ℃ flexural strength 880-1020Kg/cm2
of the compressive strength 540Kg/cm2 elongation rate 8% Brinell
hardness 65-75
V140 amine value of 375 resin with 40-60 parts per 100 parts of the
standard cure: 24 hours at room temperature or 60 ℃ 3 hours. Heat
distortion temperature of 110-115 ℃ bending strength 950Kg/cm2
compressive strength 540Kg/cm2 Brinell hardness 67-91
500 brown liquid amine value of 400 + /-20KOHmg equivalent / g at
viscosity 2-7pa.s/40 ° C per 100 parts by standard resin cured with
45-65 parts: room temperature for 24 hours or 60 ℃ 3 hours.
600 brown liquid amine value of 600 + /-20KOHmg equivalent / g at
viscosity 0.1-0.3pa.s/40 ° C per 100 parts by standard resin cured
with 20-30 parts: room temperature for 24 hours or 60 ℃ 3 hours.
650 brown-red liquid amine value of 200 + /-20KOHmg equivalent /
gram viscosity 15-50pa.s/40 ℃ (20000-40000cp/40 ℃), standard density
0.94-0.98g/cm3 25 ℃ per 100 parts resin with 40-100 parts Curing:
room temperature for 24 hours or 60 ℃ 3 hours.
651-type brown liquid amine value of 300 + /-20KOHmg equivalent / g
(Pujiang of 390-410KOHmg equivalent / g) Viscosity 2-7pa.s/40 ℃
(2000-10000cp/40 ℃) density 0.94-0.98g/cm3 25 ℃ per 100 parts by
standard resin with 45-65 parts of cure: 24 hours at room
temperature or 60 ℃ 3 hours.
3051 red brown liquid amine value of 350 + /-20KOHmg equivalent / g
of 40-100 parts per 100 parts of the standard resin cure: 24 hours
at room temperature or 60 ℃ 3 hours