Alkyl
alcohol amine H2NRNHC (R) HOH colorless liquid with 20 parts, per
100 parts by standard resin cured room temperature for 2-7 days
ERL-2793, epoxy-amine 593 of DEH-52 RCH2CH (OH) CH2NHR1NH2 Viscosity
25 ℃ 5000-13000cps per 100 parts of standard resin 20-25 copies of
specific gravity 1.07 -60 ℃ 7 days of curing at room temperature 1
hour
Modified-dicyandiamide NCCH2CH2NHRNHCH2CH2CN per 100 parts standard
resin with 20-30 parts by heat curing.
25-35 parts per 100 parts 726 of the liquid on the condensate of
phenol, formaldehyde, xylylenediamine standard resin, an amine value
of 200-350, a viscosity of 50 to -70
Per 100 parts of the liquid condensate of phenol, formaldehyde,
tetraethylenepentamine standard resin with 45 parts of amine value
of 360-450, viscosity: 90
T-31 liquid condensate of phenol, formaldehyde, diethylene triamine,
per 100 parts by standard resin with 20-25 parts amine value of
360-450, viscosity: 90
Condensates of aniline, formaldehyde, imidazolyl standard resin per
100 parts with 20 parts, curing: 85 ° C for 2 hr +150 ° C for 3
hours. The thermal deformation temperature of 176 ° C.
Maleimide, diaminodiphenyl methane prepolymer the standard resin per
100 parts with 190 parts of curing: 160 ° C for 15 minutes. At 25 ℃
bending strength was 15.3Kg/mm2, and bending strength was 1300 hours
after heating at 250 ℃ 11.9Kg/mm2.
Diethylene triamine, thiourea condensate liquid fast curing, per 100
parts by standard resin with 20-25 parts by
Triethylene tetramine, thiourea condensate liquid fast curing every
100 standard resin with 20-25
Tetraethylenepentamine, thiourea condensate liquid fast curing, per
100 parts by standard resin with 20-25 parts by
Standard resin of the hydroxymethyl diethylenetriamine
H2NC2H4NHC2H4NHCH2OH colorless liquid per 100 parts with 20 parts
low toxicity, the use of alternative ethylenediamine. Molecular
weight of 133 active hydrogen equivalent 33.2
Hydroxymethyl ethylenediamine H2NC2H4NHCH2OH colorless liquid with a
molecular weight of 15 parts per 100 parts of standard resin 90
active hydrogen equivalents of 30
Hydroxyethylethylenediamine 120 AEEA H2NC2H4NHC2H4OH colorless
liquid per 100 parts by standard resin with 16-18 parts MW 104
active hydrogen equivalent of 34 also known as N-amino ethyl
ethanolamine
Dihydroxyethyl the ethylenediamine DAEEA (HOCH2CHRNH) 2R viscous
liquid per 100 parts by standard resin with 18-20 parts of 186
molecular weight active hydrogen equivalent 36
The hydroxyethyl Diethylenetriamine H2NC2H4NHC2H4NHC2H4OH viscosity
150-300 colorless liquid with 20-30 parts per 100 parts of the
standard resin curing: +110 ° C at room temperature 4 days or 60 ℃ 1
hour 20 minutes, and the applicable period of 50 grams of room
temperature 19 minutes thermal deformation temperature 96 ° C
flexural strength 950kg/cm2, compressive strength 2790kg/cm2, room
temperature curing, slightly lower toxicity than diethylenetriamine,
heat capacity, for a short period. Molecular weight of 147 active
hydrogen equivalent of 36.2
Dihydroxyethyl Diethylenetriamine HO (CH2) 2 HNC2H4NHC2H4NHC2H4OH
colorless liquid Viscosity 150-300 the applicable period 50 with
20-30 parts per 100 parts of the standard resin curing: +110 ° C at
room temperature 4 days or 60 ℃ 1 hour 20 minutes, heat distortion
temperature of 58 ° C, g at room temperature 24 minutes flexural
strength 1000kg/cm2, compressive strength 3060kg/cm2, room
temperature curing, slightly lower toxicity than diethylenetriamine,
heat capacity, for a short period. Molecular weight of 190 active
hydrogen equivalent 63.2
Hydroxyethyl has and diamine H2NC6H12NHC2H4OH colorless liquid per
100 parts of a standard resin molecular weight of 160 with 30 parts
of active hydrogen equivalent 53.3
A cyanide ethylenediamine H2NC2H4NHC2H4 CN colorless liquid per 100
parts by standard resin with a molecular weight of 30 parts of 113
active hydrogen equivalent 37.6
A cyanoethyl to diamine H2NC6H12NHC2H4CN colorless liquid with a
molecular weight of 30 parts, per 100 parts by standard resin 169
active hydrogen equivalent 56.3
The cyanide ethylethylenediamine ZZL-0803 NCC2H4NHRNHC2H4CN
colorless liquid viscosity 90-100 proportion of 1.02 per 100
standard resin with 16-18. Molecular weight of 166 active hydrogen
equivalent 83
A cyanoethyl Diethylenetriamine 591 H2NC2H4NHC2H4 NHC2H4 CN
colorless liquid per 100 parts of the standard resin with 20-25
parts. Curing: +110 ℃ 2 hours at room temperature 4 days or 70 ℃ 3
hours, 50 g pot life at room temperature 2.5-5 hours of thermal
deformation temperature of 72-76 ℃ compressive strength 850kg/cm2,
tensile strength 510-620kg/cm2 impact strength 0.2 ft - lbs / inch
Rockwell hardness greater than 100. Room temperature curing,
slightly lower toxicity than diethylenetriamine, heat capacity, for
a short period. (Some information that heat release small for a long
period, flexibility, impact resistance, heat resistance?) Molecular
weight of 156 active hydrogen equivalent of 39
Bis cyanoethyl divinyl-amine CNC2H4 HNC2H4NHC2H4 NHC2H4 CN colorless
liquid per 100 parts by standard resin with 20-25 parts. Cure: +110
℃ 2 hours at room temperature 4 days or 70 ℃ 3 hours, apply to 50 g
at room temperature the 2.5-5 hours heat distortion temperature of
50-58 ℃ compressive strength 840-920kg/cm2, tensile strength
610-740kg/cm2 impact strength of 0.2 ft - lbs / inch Rockwell
hardness greater than 78-96. Room temperature curing, slightly lower
toxicity than diethylenetriamine, heat capacity, for a short period.
(Some information says exotherm small for a long period,
flexibility, impact resistance, heat resistance?) Molecular weight
of 208 active hydrogen equivalent of 39
Cyanoethylated xylene diamine is less than 20 ° C can be cured, low
toxicity, high thermal deformation temperature, per 100 parts by
standard resin with 20-25 parts of curing: 30 ° C for 3 hours, and a
heat distortion temperature of 102 ° C flexural strength of 15Kg /
mm2 impact strength 10 Kg-cm/cm2.
Spiro diamine with an epoxy compound, adduct synthesized by cyano
acrolein and pentaerythritol. Spiro ring diamine and then reacted
with an epoxy compound to derived. Such curing agent curing at room
temperature for a long period, the heat of reaction is low, good
color, good toughness, the impact of good performance, good heat
resistance, not to stimulate the skin can be cured in water. H2N
(CH2) 3CH (OCH2) 2C (OCH2) 2CH (CH2) 3NHCH2CHOHCH2OR. Following
formula R represents an alkyl group of C, B prefix N prefix
represents a spiro ring diamine and acrylonitrile adduct, S prefix
indicates with a 40% butanone toluene solution.
C001 viscosity 20 ° C 370 poise molecular weight of 500 per 100
parts of the amine value of 220 + / - 15 standard resin cured with
70 parts of: the a chamber warmed deformation temperature of 57.7 °
C flexural strength 10.8Kg/mm2 the flexural modulus 320Kg/mm2
tensile strength 7.15 Kg/mm2 tensile modulus 232Kg/mm2 impact
strength 14.4 Kg-cm/cm2.
C002 Viscosity 20 ° C 89 poise molecular weight of 390 per 100 parts
of the amine value of 290 + / - 15 standard resin cured with 55
parts: a chamber warmed deformation temperature of 78.6 ° C the
flexural strength 11.2Kg/mm2 bending the elastic modulus 290Kg/mm2
tensile strength 6.52 Kg/mm2 tensile modulus 194Kg/mm2 impact
strength 15.8 Kg-cm/cm2.
B001 Viscosity 20 ° C 74 poise molecular weight per 100 parts of the
the 400 amine value of 280 + / - 15 standard resin cured with 60
parts: the chamber hot heat distortion temperature 58 ° C bending
strength 11.4Kg/mm2 bending the elastic modulus 292Kg/mm2 tensile
strength 7.15 Kg/mm2 tensile modulus 235Kg/mm2 impact strength 14.4
Kg-cm/cm2.
B002 viscosity of 20 ° C 44 poise molecular weight the 340 amine
value of 330 + / - 15 per 100 parts of the standard resin cured with
50 parts: a heat distortion temperature of 80 ° C for 30 minutes 76
° C bending strength 11.5Kg/mm2 flexural modulus 291Kg/mm2 tensile
The elastic modulus 216Kg/mm2 strength 7.30Kg/mm2 tensile impact
strength 15.8 Kg-cm/cm2.
N001 Viscosity 20 ° C 29 poise molecular weight per 100 parts of the
330 amine value of 340 + / - 15 standard resin cured with 60 parts:
a heat distortion temperature of 60 ° C for 30 minutes 55 ° C
bending strength 11.6Kg/mm2 flexural modulus 298Kg/mm2 tensile The
elastic modulus 100Kg/mm2 strength 7.97Kg/mm2 tensile impact
strength 15.8 Kg-cm/cm2.
N002 Viscosity 20 ° C 20 poise molecular weight the 330 amine value
of 370 + / - 15 per 100 parts of standard resin cured with 50 parts:
the chamber warmed deformation temperature 80.7 ° C flexural
strength the elastic modulus 297Kg/mm2 is 12.4Kg/mm2 bending tensile
strength of 6.85 Kg/mm2 tensile modulus 107Kg/mm2 impact strength
15.8 Kg-cm/cm2.
S002 viscosity 20 ° C 350 parked molecular weight 1500 amine value
of 145 + / - 15
Diketone acrylamide adduct CH2CHCONHC (CH3) 2CH2CNRCH3 it is
obtained from acetone and Acrylonitrile diketone acrylamide (DAA),
and the primary amine obtained amine adduct. Non-toxic, easy to
operate, the resulting product is a transparent, weather resistance,
good water resistance.
Condensing the amine (xylylenediamine condensate) standard resin per
100 parts of the 105 light brown liquid with 12-14 parts. Can be
cured at room temperature, the product was both high heat distortion
temperature of 140 ° C, has a good toughness. 2x135 molecular weight
of 253 active hydrogen equivalent 60
590 brown-black viscous liquid per 100 parts of standard resin with
the 12-20 copies toxicity, toughness molecular weight of 269 active
hydrogen equivalent of 40
593,855 a pale yellow liquid with a viscosity of 20-25 parts per 100
parts of standard resin small, low toxicity, the use of a short
period of rapid curing at room temperature, the toughness of the
cured product is preferably molecular weight of 233 active hydrogen
equivalent 40-50
Standard resin per 100 parts of the 701 T-33 brown-red viscous
liquid with strict requirements on the amount of 25-35 were
volatile, can be cured in 0-15 ℃ under humid conditions. Molecular
weight of 226 active hydrogen equivalent 40-50
702 T-32 red brown viscous liquid per 100 parts of the standard
resin with 30-40 parts by volatile dosage strict requirements, can
be cured under moist conditions. The flexural strength 2500Kg/cm2
impact strength 190Kg/cm2 MW 217 active hydrogen equivalents 40-50
703 T-31 brown-red viscous liquid viscosity 1100-1300mpa.s25 ℃
proportion of 1.08-1.09g/cm3 25 ° C Refractive index 1.5250-1.5300
amine value of 460-480KOHmg equivalents / g standard resin with
20-25 parts per 100 parts of volatile small, the amount of strict
requirements can be cured under moist conditions. Flexural strength
2500Kg/cm2 impact strength 136Kg/cm2 tensile strength of 150kg/cm2
MW 167 active hydrogen equivalent 40-50
Diaminodiphenyl methane, methyl iso-butyl ketone adduct per 100
parts of the standard resin with 38 parts of 25 ° C for 24 hours.